ASTM A265 PDF

ASTM A ASME SA “Standard Specification for Nickel and Nickel-Base Alloy-Clad Steel. Plate”. “STANDARD SPECIFICATION FOR NICKEL AND. Buy ASTM A SPECIFICATION FOR NICKEL AND NICKEL-BASE ALLOY-CLAD STEEL PLATE from SAI Global. Designation: A − 12Standard Specification for Nickel and Nickel-Base Alloy- Clad Steel Plate1 This standard is issued unde.

Author: Maumi Yom
Country: Antigua & Barbuda
Language: English (Spanish)
Genre: Career
Published (Last): 5 January 2010
Pages: 397
PDF File Size: 11.67 Mb
ePub File Size: 3.32 Mb
ISBN: 728-6-11765-748-5
Downloads: 39756
Price: Free* [*Free Regsitration Required]
Uploader: Kajijar

The surface condition of the repaired area shall be restored to a condition similar to the rest of the cladding. Repair of Cladding by Welding The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. Workmanship Finish, and Appearance If wet chemical procedures are used, millings may be taken only when the composite plate thickness is sufficient to permit obtaining millings without danger of contamination from the adjacent layer.

The material is generally intended for pressure vessel use but may be used in other structural applications where corrosion resistance of the w265 is of prime importance. Materials and Manufacture 5. The base metal shall be carbon steel or low-alloy steel conforming to sstm specifications for steels for either pressure vessels or for general structural applications. Approved May 1, ast Other tests may be performed by agreement between the supplier and the purchaser.

The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. ASTM International takes no position respecting the validity of any asrm rights asserted in connection with any item mentioned in this standard.

The sides of the bend test specimen used for bond strength determination may have the corners rounded to a radius not over 1? Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend. Last previous edition approved in as A — The base metal shall conform to the chemical requirements of the speci?

  CAPIRE IL DESIGN ANDREA BRANZI PDF

The nickel or nickel-base alloy cladding metal shall conform to prescribed chemical composition. Several of those considered suitable for use with this speci?

ASTM A – 03 Standard Specification for Nickel and Nickel-Base Alloy-Clad Steel Plate

Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters. Link to Active This link will always route to the current Active version of the standard. In reducing the thickness of the specimen, both the alloy 3 Metric Equivalents in. Greater separation shall be cause for asgm.

Current edition approved May 1, Originally approved in If you feel that your comments have not received a fair hearing you should make your views known to the ASTM Committee on Standards, at the address shown below.

NOTE 3—The dimension t is the thickness of the test specimen as provided for in the applicable material speci? Individual reprints single or multiple copies of this a625 may be obtained by contacting ASTM at the above address or at phonefaxor service astm. Product and chemical analyses shall be performed on the cladding alloy and a25 accomplished by wet chemical or instrumental procedures.

ASTM A265 Clad Plate

It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date. Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard. The minimum cladding thickness for shear testing shall be 0.

Method of test and acceptance standard shall be as agreed upon between the purchaser and the manufacturer. If spectrometric procedures are used, the sample shall be exposed on the center line of the cladding when there is sufficient cladding thickness available so that there is no contamination from the adjacent base metal. Historical Version s – view previous versions of standard. The material shall be cleaned and sufficient millings taken to represent the full cross-section of the remainder.

  CALCULO DIFERENCIAL E INTEGRAL LEITHOLD 7 EDICION PDF

This specification covers the standard for plate of a carbon steel or low-alloy steel base to which is integrally and continuously bonded on one or both sides a layer of nickel or nickel-base alloy. A — 09 Standard Speci? This standard has been approved for use by agencies of the Department of Defense. The shear test, when speci? Historical Version s – view previous versions of standard Translated Version s: Gage Length cladding and the base steel shall be machined so as to maintain the same ratio of clad metal to base steel as is maintained in the plate, except that the thickness of the clad material need not be reduced below 1?

These bend tests shall be made in the manner of the tension tests indicated in Fig.

Sstm none has been speci? This standard is subject to revision at any time by the responsible technical committee and must be reviewed every?

The material is generally intended for pressure vessel use but may be used in other structural applications where corrosion resistance of the alloy is of prime importance.

Reports shall include the results of ultrasonic inspection when Supplementary Requirement S12 is speci? Ultrasonic Examination in accordance with Speci? Each specimen shall be in the? For purposes of de? NOTE 2—Punch marks for measuring elongation after fracture shall be made on the? General Requirements for Delivery Areas within 1 in.

The tensile properties thus determined shall meet the base steel requirements.